Two-component 1:1 epoxy for repairing and protecting equipment exposed to abrasion, impact, and vibration caused by fine particles, with functional cure in one hour.
Precise, durable repair of localized wear and damage on steel, ceramic, and concrete surfaces, including vertical and overhead applications.
As fine-particle wear progresses, equipment surfaces lose thickness and develop weak points such as microcracks, porosity, and localized damage. These conditions can lead to leaks, reduced efficiency, and unplanned downtime. In addition, in difficult-to-access areas, a repair material that sags or cannot maintain a controlled application thickness may leave uneven coverage, allowing damage to recur and progress.
DURAFAST® MX2 is designed to repair and protect surfaces exposed to abrasion, impact, and vibration from fine particles. Its fast-curing, non-sag consistency enables controlled application on vertical and overhead surfaces with functional cure in one hour.
Precision and application control with a fine finish: this epoxy resin provides effective protection against fine-particle wear, with non-sag performance and reduced time to return to service.
One solution for multiple surfaces.
Reliable, long-lasting protection under demanding wear conditions.
Control and coverage on vertical and overhead surfaces.
Fine finish and precise repair of localized damage and small voids.
Return to operation in 1 hour.
Designed to operate effectively down to –15 °C (with DURAFAST® accelerator).
Simple, controlled on-site preparation.
An alternative for reducing curing times in cold conditions and emergencies.
Common applications for protecting and rebuilding equipment exposed to impact and abrasion from coarse material.
Cyclones, hydrocyclones, and pumps
Lining and sealing in complex geometries: internal wear, leaks, and loss of thickness.
Ducts, pipes, and elbows
Protection in turbulent-flow areas: progressive erosion that affects performance and continuity.
Mill discharge areas and hoppers
Restoration of surfaces exposed to impact and abrasion: severe wear and downtime.
Conveyor systems and wear plates
Lining at transfer and conveying points: continuous friction, thinning, and substrate exposure.
Data to evaluate performance, working times, and application conditions. For complete details, download the technical data sheet.
Pot life at (25 °C/77 °F)
35 minutos
Functional cure, light loads
60 minutes
Mix ratio
1:1
Hardness after cure
87,0 SHORE D
Dry temperature resistance
150 °C/302 °F
Tensile strength
29,65 N/mm² / 4.300 psi
Compressive strength
75,84 N/mm² / 11.000 psi
Real applications and results that support the use of DURAFAST® MX2.
PROBLEM:
Irregular gearmotor alignment caused by metal-to-metal wear. The concave areas required rebuilding to correct alignment and prevent further deterioration.
SOLUTION:
The repair was completed in 1.5 hours. DURAFAST® MX2 provided a rapid, high-strength solution with excellent adhesion and efficient curing under restricted working conditions.
RESULT:
DURAFAST® MX2 extended component service life while reducing maintenance requirements and downtime. After 48 days in service, wear remained below 2 mm, indicating effective protection for more than five months.
Contact our specialists. They will help you find the best solution based on the equipment, problem, or urgent situation you need to address.
Our products support a wide range of applications. Tell us about your operation and current needs, and our team will help identify the right product, service, or technical solution.
Brasil
Av. Niágara, 398,
Jardim Canadá, Nova Lima-MG, Brasil, 34007-652
+55 31 3581 3545
Panama
Zona Franca PanaPark, Av. Panamericana, Corregimiento 24 de diciembre, Galería 22
Ciudad de Panamá
+507 310 8547
For international Sales:
Em breve, nossa equipe comercial entrará em contato com você.
Verifique sua caixa de entrada (e a pasta de spam ou promoções) para garantir que você receba as informações.